Makhalidwe a Tungsten Metal Powder

Kuchita kwa ufa wa tungsten kumakhudza kwambiri ntchito yokonza ndi khalidwe lazinthu zotsatila. Chifukwa chake, gawo lolimba la aloyi ndi gawo lopangira zinthu za tungsten zapereka zofunikira zofananira pakuyera kwamankhwala komanso mawonekedwe amtundu wa ufa wa tungsten, makamaka zomwe zimafunikira pazakuthupi zikukulirakulira. 

Chemical chiyero

Mukapanga zopangira simenti ya carbide ndi tungsten, kuyeretsedwa kwa mankhwala a tungsten ufa kumafunika kukhala okwera kwambiri. Zotsalira zotsalira zonyansa mu tungsten ufa zimakhudza momwe zimagwirira ntchito komanso magwiridwe antchito azinthu. Chikokacho ndi chovuta kwambiri, ndipo china chimakhala chovulaza komanso chopindulitsa. Kafukufuku wamakono akusonyeza kuti Ca, Mg, P, As, Si, S, Fe, Ni, Cu, Al, ndi Mo akhoza kuchepetsa mphamvu ya alloy, pamene K ndi Na zimalimbikitsa kukula kwa mbewu za WC. V ndi Cr, kumbali ina, amalepheretsa kukula kwa mbewu. Ngati zomwe zili mu WO mu WO zimaposa 0.5%, zidzachepetsa mphamvu ya flexural ya alloy. M'mitundu yambiri ya ufa wa tungsten yomwe imapangidwa pano, zomwe zili muzitsulo zotsalira zazitsulo (kupatula zomwe zawonjezeredwa ngati zowonjezera) zimakhala m'magulu angapo pa zikwi khumi mpaka magawo ochepa pa zana lililonse. 

Oxygen mu tungsten ufa amatha kuchitapo kanthu ndi carbides, kuyamwa kaboni kuchokera ku carbides ndikupangitsa decarburization ya simenti ya carbide. Pamene aloyi yawonongeka kwambiri, gawo la γ likuwonekera, kupangitsa kuti alloy brittle. Mpweya wotulutsidwa kuchokera kuzomwe umawonjezera porosity ya alloy ndikuchepetsa mphamvu zake. Kutengera njira zosiyanasiyana zochepetsera ndi zida, mpweya wa okosijeni mu ufa wa tungsten nthawi zambiri umakhala pakati pa 0.05% ndi 0.5%, ndipo umawonjezeka ndi kuchepa kwa tinthu tating'onoting'ono tating'ono komanso kuchuluka kwa malo enieni. Chifukwa chake, kufunikira kwa okosijeni mu ufa wa tungsten wopangidwa bwino kuyenera kumasuka bwino. Zofunikira za chiyero cha mankhwala a tungsten ufa zikuwonetsedwa mu Table 4-1, ndipo zofunikira za okosijeni zikuwonetsedwa mu Table 4-2.

Zinthu zosadetsedwa mu ufa wa tungsten zitha kubwera kuchokera kuzinthu zopangira kapena kuyambitsidwa panthawi yopanga. Choncho, kuteteza kuipitsidwa kwa zipangizo panthawiyi ndikofunika kwambiri. Mwachitsanzo, popanga ufa wa tungsten pogwiritsa ntchito APT monga zopangira, zidazo zimagwirizana mwachindunji ndi ng'anjo ya calcining, kuchepetsa machubu a ng'anjo, ndi crucibles, zomwe zimapangitsa kuwonjezeka kwa zinthu zonyansa monga Fe, Ni, Cr, ndi Si, ndi kuchepa kwa chiyero cha mankhwala. Zomwe zili nazo zikafika pamlingo wina kapena zikuphatikiza kukula kokwanira, zitha kukhala magwero a zolakwika pakukonzedwa kapena kugwiritsidwa ntchito. Choncho, kuonetsetsa chiyero cha ufa wa tungsten, kuphatikizapo kulamulira mosamalitsa ubwino wa APT yamtengo wapatali, ndikofunikanso kuti tipewe kuipitsidwa panthawiyi. 

2. Katundu Wathupi

The thupi katundu zitsulo tungsten ufa makamaka monga pafupifupi tinthu kukula, tinthu kukula kugawa, tinthu aggregation digiri, tinthu morphology, enieni pamwamba dera, chochuluka kachulukidwe, tikaumbike kachulukidwe, ndi Hall otaya mlingo, etc. 

(Avereji ya kukula kwa tinthu ndi kagawo kakang'ono kagawidwe)

Kaya ndi cemented carbide kapena tungsten mankhwala, pali zofunika okhwima pafupifupi tinthu kukula ndi tinthu kukula kugawa tungsten ufa. M'munda wa simenti carbide, tinthu kukula ndi tinthu kukula kugawa W ufa mwachindunji zimakhudza tinthu kukula ndi tinthu kukula kugawa kwa opangidwa WC ufa. Kukula kwa tinthu ting'onoting'ono kwa ufa wa WC kumakhudzanso magwiridwe antchito a carbide. 

Kafukufuku wapeza kuti katundu wa WC ufa amaletsedwa ndi a W powder. Pambuyo pa ufa wa W ndi carbonized kupanga WC, kukula kwa tinthu kumasintha pang'ono. Kupanga WC ufa wa coarse, sing'anga ndi zabwino tinthu kukula, coarse, sing'anga ndi chabwino tinthu W ufa ayenera kugwiritsidwa ntchito. Uneven W ufa carbonization umabweretsa WC ufa wosafanana. Kusintha kwa tinthu tating'onoting'ono tating'onoting'ono pambuyo pa carbonization ya coarse, sing'anga ndi tinthu tating'onoting'ono ta W tikuwonetsedwa mu Table 4-3.

Zofunikira za kukula kwa tinthu ta tungsten kumasiyana pakati pa ogwiritsa ntchito osiyanasiyana. Pakuti zolimba aloyi kumunda, kwa mitundu yosiyanasiyana ya aloyi zolimba ntchito zolinga zosiyanasiyana, chifukwa osiyana tinthu kukula kwa WC ufa ntchito, pali zofunika zosiyanasiyana kwa pafupifupi tinthu kukula ndi tinthu kukula zikuchokera ya zopangira W ufa. Zida zonse zodulira zimafunikira ufa wa W ndi ufa wa WC kuti ukhale ndi kukula kwa tinthu tating'onoting'ono komanso kagawo kakang'ono kakang'ono. Zida zogwirira ntchito zimafuna ufa wa W ndi ufa wa WC kuti ukhale wokhuthala, ndikugawa tinthu tambirimbiri. Wapakati tinthu kukula ntchito pokonzekera coarse-grained WC ndi 25.8 μm. Kugawidwa kwa tinthu tating'ono ta W ufa kukuwonetsedwa mu Chithunzi 4-1.

Pakuti tungsten zakuthupi processing, pafupifupi tinthu kukula ndi tinthu kukula kugawa tungsten ufa zimakhudza kukanikiza ntchito ya wotsatira mankhwala, kachulukidwe wa thupi wobiriwira (amatchedwanso mbamuikha thupi), ndi sintering ntchito. Tinthu tating'onoting'ono tating'onoting'ono komanso mawonekedwe ovuta kwambiri kumapangitsa kukangana kwakukulu pakati pa tinthu tating'onoting'ono, zomwe zimapangitsa kuchepa kwa kachulukidwe ka thupi lobiriwira. The yopapatiza tinthu kukula kugawa, ndi momasuka kwambiri particles anakonza. A ambiri tinthu kukula kugawa, kapena ngakhale kusakaniza ufa zosiyanasiyana pafupifupi tinthu kukula kwake, akhoza kukwaniritsa bwino tinthu makonzedwe ndi kupeza apamwamba wobiriwira thupi mphamvu. M'munda wopangira zinthu za tungsten, kukula kwa tinthu tating'ono ta tungsten nthawi zambiri kumafunika kukhala mkati mwa 2 mpaka 6 μm. 

Pali njira zambiri zodziwira kukula kwa tinthu tating'ono ndi kugawa kwa tinthu. Zida za Fischer ndi laser particle size analyzer amagwiritsidwa ntchito kwambiri mu tungsten ufa. Komabe, chifukwa cha mfundo zosiyana za njira ziwirizi zoyezera, miyeso yoyezera yomwe imachokera ku ufa womwewo ukhoza kusiyana. Chifukwa chake, kukula kwa tinthu tating'ono ting'onoting'ono kuyenera kunenedwa ngati Fischer's average particle size or laser average particle size. Kuphatikiza apo, ziyenera kudziwidwa kuti "boma loperekedwa" tungsten ufa nthawi zambiri amakhala ndi magawo osiyanasiyana, omwe amakhudzana ndi momwe amapangira. Wapakati tinthu kukula tungsten ufa kuyeza ntchito zitsanzo akhoza kusiyana kwenikweni tinthu kukula kwa ufa. Mwachitsanzo, kukula kwa tinthu ting'onoting'ono ta ufa wa tungsten mu "boma loperekedwa" ndi 1-2 μm, ndipo pambuyo pa depolymerization ndi kubalalitsidwa, mtengowo umatsikira ku 0.4-0.5 μm. Pakuti tungsten ufa ndi kukula tinthu mu osiyanasiyana 1-10 μm, nthawi zambiri, kuyeza "boma anapereka" tinthu kukula akhoza kukwaniritsa zofunika kupanga. Pakuti submicron tungsten ufa ndi coarser tungsten ufa, kuti molondola amasonyeza kukula kwa particles, "akupera boma" zitsanzo ayenera kugwiritsidwa ntchito pafupifupi tinthu kukula ndi tinthu kukula kugawa mayesero. 

TKugawa kwa tinthu tating'ono ta tungsten kumagwirizana ndi kukula kwake. Nthawi zambiri, kukula kwa tinthu tating'onoting'ono ta tungsten ufa, kufalikira kwa tinthu tating'onoting'ono. Pakuti anapatsidwa tinthu kukula, kupanga, njira monga ntchito chonyowa haidrojeni kapena kuwonjezera alkali zitsulo mankhwala kwa tungsten okusayidi angapangitse tinthu kukula lalikulu ndi kulamulira tinthu kukula yogawa osiyanasiyana movutikira kwambiri. Kudziwitsa kukula kwa tinthu nthawi zambiri kumachitika pogwiritsa ntchito zitsanzo za "ground state". 

Kukula kwapakati kwa tungsten ufa nthawi zambiri kumawonetsedwa ndi mainchesi ake (mu ma micrometer). Komabe, muzochita zopanga, malingaliro ena a semi-quantitative amagwiritsidwa ntchito nthawi zambiri. Magulu odziwika bwino ndi awa: 

Tinthu tating'onoting'ono kwambiri: Avereji ya tinthu tating'ono > 30 μm; 

30 μm; 

Coarse particles: Avereji ya tinthu tating'onoting'ono 10 mpaka 30 μm; 

Sing'anga-kakulidwe particles: Avereji tinthu kukula 3 mpaka 10 μm; 

Fine particles: Avereji tinthu kukula 0,5 - 3 μm; 

Ultrafine particles: pafupifupi tinthu kukula

(2) Digiri yophatikizira

The aggregation digiri ya ufa nthawi zambiri yodziwika ndi kusiyana tinthu kukula pakati "amaperekedwa boma" ufa ndi "pansi boma" ufa. Madigiri ophatikiza a ufa wa tungsten nthawi zambiri amakhala apamwamba kuposa a ufa wa tungsten. Pakupanga zinthu za tungsten, digiri ya aggregation imakhudza mwachindunji mphamvu ya chidutswa chobiriwira. Pakupanga kwa WC, kuchuluka kwa ufa wa ufa kumakhudza kufanana kwa kugawa mpweya. 

(3) Tinthu tating'onoting'ono

Tinthu tating'ono ting'onoting'ono ta tungsten ufa timakhudza kulimbikira kwake komanso mphamvu ya thupi lobiriwira. Osakhazikika tinthu morphology kumabweretsa interlocking pakati particles, potero utithandize mphamvu ya thupi wobiriwira. Ufa wozungulira wa tungsten uli ndi madzi abwino ndipo ndi oyenera kupopera mankhwala. Mofananamo, pokonzekera WC, morphology ya tungsten powder imakhudzanso kapangidwe ka ufa wa WC. 

(4) Malo Odziwika Pamwamba

Malo onse omwe ali ndi unit mass of tungsten powder amatchedwa malo enieni a tungsten powder, omwe nthawi zambiri amawonetsedwa m'magulu a m2 · g-1. Malo enieni a tungsten ufa nthawi zambiri amachokera ku 0.01 mpaka 12 m2 · g-1. Imawonetsa mosadukiza kukula kwa tinthu tating'ono ndi mawonekedwe a ufa wa tungsten ndipo ndi chizindikiro chofunikira pakuwunika ntchito ya sintering, mikhalidwe yakusungunuka, komanso kuthekera kochita ndi zinthu zamafuta komanso zolimba panthawi ya carbonization ya ufa wa tungsten. 

(5) Kachulukidwe kotayirira komanso kachulukidwe kakang'ono

The lotayirira kachulukidwe ndi tikaumbike kachulukidwe tungsten ufa kuwonjezeka ndi kuwonjezeka pafupifupi tinthu kukula kwa ufa. Ubale pakati pa kusachulukira kwa ufa wa tungsten wopangidwa ndi fakitale inayake ndi kukula kwake kwapakati pa Fischers kukuwonetsedwa mu Table 4-4. The yopapatiza tinthu kukula kugawa ufa, ndi zovuta kwambiri tinthu morphology, ndipo kwambiri aggregation, ang'onoang'ono lotayirira kachulukidwe. Kawirikawiri, magawo a ndondomeko yochepetsera akhoza kusinthidwa kuti aziwongolera.

(6) Madzi amadzimadzi

Kuchuluka kwa tungsten ufa kumatengera kukula kwa tinthu, kukula kwa tinthu, ndi kapangidwe kake. Kuchuluka kwa tinthu ting'onoting'ono twa ufa, tinthu tating'onoting'ono tozungulira, komanso kusalala pamwamba, kumapangitsa kuti madzi azisungunuka. Kuchuluka kwa ufa wa tungsten nthawi zambiri kumayesedwa ndi kuchuluka kwa Hall flow, komwe kumawonetsedwa ngati nthawi yomwe 50g ya ufa wa tungsten umayenda kudzera pabowo laling'ono lomwe lili mu mita ya Hall flow. Kutsekemera kwa ufa kumakhudza mwachindunji kukweza kwa volumetric panthawi yokakamiza komanso kufanana kwa kachulukidwe kakufa. 

(7)Compressibility

Compressibility imatanthawuza kuthekera kwa ufa wa tungsten kuti utsindikidwe pansi pamikhalidwe yodziwika bwino. Nthawi zambiri amayezedwa mu zisamere pachakudya chokhazikika pamikhalidwe yodziwika bwino, ndipo imawonetsedwa ndi kachulukidwe ka ufa wa mankhwala oponderezedwa pansi pa kukakamizidwa komweko. Itha kuyimiridwanso ndi graph yokhotakhota yomwe ikuwonetsa kusintha kwa kachulukidwe kazinthu zopanikizidwa ndikukakamiza. 

(8) Kukhazikika